材料描述
特性:透明高光泽热稳定耐高温黑种
应用领域:食品包装食品服务领域食品容器造粒注塑
颜色:--
等级:注塑级
物性表
密度 | ASTM D792/ISO 1183 | 1.06 | kg·cm/cm(J/M)ft·lb/in | |
熔融指数(流动系数) | ASTM D1238/ISO 1133 | 2.8 | g/10min | |
熔融指数(流动系数) | ASTM D1238/ISO 1133 | 14 | g/10min |
熔融指数 | 条件I | ASTM D-1238 | 14.0 | g/10min |
熔融指数 | 条件G | ASTM D-1238 | 2.8 | g/10min |
洛氏硬度 | ASTM D-785 | 83 | M | |
弯曲强度 | ASTM D-790 | 1000(14200) | kg/cm2(lb/in2) | |
弯曲弹性率 | ASTM D-790 | 3.5(5.0) | 10kg/cm2(10lb/in2) | |
伸长率 | ASTM D-638 | 3.0 | % | |
拉伸强度 | ASTM D638/ISO 527 | 710 | kg/cm²(MPa)[Lb/in²] | |
洛氏硬度 | ASTM D785 | M-83 | ||
弯曲强度 | ASTM D790/ISO 178 | 1000 | kg/cm²(MPa)[Lb/in²] | |
引张强度 | ASTM D-638 | 710(10060) | kg/cm2(lb/in2) | |
IZOD冲击强度 | 1/8〃 | ASTM D-256 | 1.8(0.33) | kg.cm/cm(ft.ld/in) |
IZOD 缺口冲击强度 | ASTM D256/ISO 179 | 1.7 | kg·cm/cm(J/M)ft·lb/in | |
IZOD 缺口冲击强度 | ASTM D256/ISO 179 | 0.31 | kg·cm/cm(J/M)ft·lb/in | |
IZOD 缺口冲击强度 | ASTM D256/ISO 179 | 1.8 | kg·cm/cm(J/M)ft·lb/in | |
IZOD 缺口冲击强度 | ASTM D256/ISO 179 | 0.33 | kg·cm/cm(J/M)ft·lb/in | |
IZOD冲击强度 | 1/4〃 | ASTM D-256 | 1.7(0.31) | kg.cm/cm(ft.ld/in) |
燃烧性(率) | UL94 | HB | ||
热变形温度 | ASTM D648/ISO 75 | 100(212) | ℃(℉) | |
维卡软化点 | ASTM D1525/ISO R306 | 104 | ℃(℉) | |
热变形温度 | ASTM D-648 | 100(212) | °C | |
维卡软化点 | ASTM D-1525 | 104(219) | ℃(℉) | |
热变形温度 | ASTM D-648 | 90(194) | ℉ | |
燃烧性 | 1/16"HB |
其他新闻
- AS(SAN)台湾台化NF2200AE现货供应 2024-11-22
- 众欢供应POM德国巴斯夫FK66003 2024-11-22
- 众欢供应POM德国巴斯夫E3120BM 2024-11-22
- ABS/PBT 日本大赛璐 BM5544 2024-11-22
- ABS/PA 韩国英力士苯领 NM-21EF 2024-11-22
- SMMA 美国英力士 NAS30 2024-11-22
- PTFE 日本大金 F-201 2024-11-22
- PPS日本东丽A504X90 2024-11-22
- PPO 基础创新塑料(美国) SE1X-701 2024-11-22
- PPE 日本旭化成 540Z BK 2024-11-22
- PPA 美国杜邦 HTN51G35HSL 2024-11-22
- PES 德国巴斯夫 E2010 2024-11-22
- PEI 基础创新塑料(美国) 1000-1000 2024-11-22
- PEEK 英国威格斯 450G 2024-11-22
- PA9T 日本可乐丽 G1300H 2024-11-22