PA66日本旭化成1300S代理商
物性表
密度 | ASTM D792/ISO 1183 | 1.14 | ||
吸水率 23℃/24H | ASTM D570/ISO 62 | 2.5 | % |
收缩率 | MD2.0mm | ASTMD995 | 1.3 | % |
收缩率 | TD2.0mm | ASTMD995 | 2.0 | % |
吸水率 | (23°C,24hr) | ASTMD570 | 2.5 | % |
收缩率 | 干 | 旭化成方法 | 1.3-2.0 | % |
悬臂梁式缺口冲击强度 | 干(湿) | ASTM D-256 | 39(147) | J/m |
拉伸强度 | 干(湿) | ASTM D-638 | 79(57) | Mpa |
断裂延伸率 | 干(湿) | ASTM D-638 | 50(250) | % |
洛氏硬度 | 干(湿) | ASTM D-785 | 120(108) | R scale |
抗挠强度 | 干(湿) | ASTM D-790 | 118(54) | Mpa |
抗挠系数 | 干(湿) | ASTM D-790 | 2.8(1.2) | GPa |
磨耗率 | 湿 | ASTM D-1044 | 7 | |
断裂伸长率 | 23°C | ASTMD638 | 50 | % |
弯曲强度 | 23°C | ASTMD790 | 118 | Mpa |
弯曲模量 | 23°C | ASTMD790 | 2800 | Mpa |
悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 39 | J/m |
断裂伸长率 | ASTM D638/ISO 527 | 50 | % | |
弯曲模量 | ASTM D790/ISO 178 | 2790 | kg·cm/cm(J/M)ft·lb/in | |
弯曲强度 | ASTM D790/ISO 178 | 118 | kg·cm/cm(J/M)ft·lb/in | |
洛氏硬度 | 干(湿) | ASTM D-785 | 80(55) | M Scale |
拉伸强度 | 23°C | ASTMD638 | 79 | Mpa |
Charpy冲击强度 | ASTM D256/ISO 179 | 39 | kg·cm/cm(J/M)ft·lb/in |
热变形温度 | 0.46MPa,干 | ASTM D-648 | 230 | °C |
热变形温度 | 1.82MPa,干 | ASTM D-648 | 70 | °C |
阻燃性 | 干 | UL 94 | V-2 | |
线性膨胀系数 | 干 | ASTM D-696 | 8 | |
导热率 | 干 | 0.2 | W/(m.K) | |
比热容 | 干 | 1670 | J/(kg.k) | |
燃烧性(率) | UL94 | v-2 | ||
热变形温度 | ASTM D648/ISO 75 | 230 | ℃(℉) | |
线性膨胀系数 | ASTM D696/ISO 11359 | 8 | mm/mm.℃ | |
热变形温度 | 0.45MPa未退火 | ASTMD648 | 230 | °C |
热变形温度 | 1.80MPa未退火 | ASTMD648 | 70 | °C |
线膨胀系数 | 导热系数 | JISR2618 | 0.2 | W/m/K |
线膨胀系数 | 比热 | 1670 | J/kg/°C |
发布时间:2024-11-14
展开全文
其他新闻
- PA66河南神马尼龙EPR27代理商 2024-11-14
- PC/ABS 基础创新塑料(南沙) C1200HF供应商 2024-11-14
- PC/ABS 上海科思创(拜耳) T45 PG 000000供应商 2024-11-14
- PC/ABS 德国科思创(拜耳) T65XF 901510供应商 2024-11-14
- PC/ABS 基础创新塑料(南沙) C2800-701供应商 2024-11-14
- PC/ABS 台湾奇美 PC-365供应商 2024-11-14
- PC/ABS 基础创新塑料(南沙) MC1300-100供应商 2024-11-14
- PC/ABS 台湾奇美 PC-510供应商 2024-11-14
- PC/ABS 广州LG GN5001RFH供应商 2024-11-14
- PC/ABS 基础创新塑料(美国) C2950-111供应商 2024-11-14