ASA台湾奇美PW-957
物性表
密度 | ASTM D792/ISO 1183 | 1.07 | ||
熔融指数(流动系数) | ASTM D1238/ISO 1133 | 28 | g/10min |
熔体质量流动速率 | 220°C/10.0kg | ASTMD1238 | 23 | g/10min |
熔体体积流动速率 | 220°C/10.0kg | ISO1133 | 23.0 | cm3/10min |
收缩率 | ISO294-4 | 0.40to0.70 | % |
抗张强度3 | 屈服 | ASTMD638 | 43.0 | Mpa |
拉伸应力 | 屈服 | ISO527-2/50 | 46.0 | Mpa |
拉伸应力 | 断裂 | ISO527-2/50 | 33.0 | Mpa |
伸长率4 | 断裂 | ASTMD638 | 55 | % |
拉伸应变 | 断裂 | ISO527-2/50 | 20 | % |
弯曲模量4 | ASTMD790 | 2160 | Mpa | |
拉伸强度 | ASTM D638/ISO 527 | 440 | kg/cm²(MPa)[Lb/in²] | |
弯曲强度 | ASTM D790/ISO 178 | 650 | kg/cm²(MPa)[Lb/in²] | |
弯曲模量5 | ISO178 | 2200 | Mpa | |
弯曲强度4 | ASTMD790 | 63.3 | Mpa | |
弯曲应力5 | ISO178 | 67.0 | Mpa | |
引张强度 | ASTM D-638 | 420 | kg/cm | |
弯曲强度 | ASTM D-790 | 550 | kg/cm | |
IZOD冲击强度 | 1/8" | ASTM D-256 | 15 | kg.cm/cm |
IZOD 缺口冲击强度 | ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in | |
IZOD 缺口冲击强度 | ASTM D256/ISO 179 | 15 | kg·cm/cm(J/M)ft·lb/in |
发布时间:2024-12-25
展开全文
其他新闻
- PBT聚对苯二甲酸丁二醇酯483 BK 2024-12-25
- LDPE 中石化2426K 低密度聚乙烯材料 2024-12-25
- HDPE 韩国LG ME9180 聚乙烯材料 2024-12-25
- PA6 台湾DSM101C2 高性能聚酰胺材料 2024-12-25
- PA66 新加坡杜邦101L 高性能尼龙材料 2024-12-25
- PP 台塑3015 高性能聚丙烯材料 2024-12-25
- PC/ABS 台化AC310 高性能合金材料 2024-12-25
- PC韩国乐天化学PC-110 高性能聚碳酸酯代理商 2024-12-25
- ABS奇美PA-758工程塑料产品 2024-12-25
- 突破技术边界,PA66新加坡杜邦 101F NC010,打造卓越品质! 2024-12-25